A2017-T4アルミニウム合金の回転曲げ疲労強度に及ぼす無電解Ni-Pめっきの影響

DOI DOI Web Site Web Site Web Site ほか1件をすべて表示 一部だけ表示 被引用文献6件 参考文献20件 オープンアクセス

書誌事項

タイトル別名
  • Effect of electroless Ni-P plating on rotary bending fatigue strength of A2017-T4 aluminum alloy
  • A2017-T4 アルミニウム ゴウキン ノ カイテン マゲ ヒロウ キョウド ニ オヨボス ムデンカイ Ni-Pメッキ ノ エイキョウ

この論文をさがす

説明

<p>In this study, A2017-T4 aluminum alloy was plated with electroless Ni-P with different phosphorus content and rotary bending fatigue test was conducted to investigate the effect of hydrogen by plating on fatigue properties. The fatigue strength of the low-phosphorus type Ni-P plated specimen was higher than that of the untreated specimen, while that of the high-phosphorus type plated specimen was much lower. It is clear that the fatigue strength differs greatly depending on the phosphorus content in the plating film. The decrease in fatigue strength of the high phosphorus type plating specimen was attributed to hydrogen induced by plating from hydrogen analysis. Thus, despite the previous report that 2000 series aluminum alloys do not exhibit hydrogen embrittlement in slow strain rate tensile tests under wet condition, it was found that A2017-T4 aluminum alloy undergo hydrogen embrittlement when the alloy is plated with high-phosphorus type electroless Ni-P and fatigue-tested on rotary bending machine.</p>

収録刊行物

  • 軽金属

    軽金属 71 (10), 450-454, 2021-10-15

    一般社団法人 軽金属学会

被引用文献 (6)*注記

もっと見る

参考文献 (20)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ