ヘテロナノ組織Cu–Be系合金の組織と力学的特性

DOI Web Site オープンアクセス

書誌事項

タイトル別名
  • Microstructure and Mechanical Properties of the Heterogeneous–Nano Structured Cu–Be System Alloys
  • ヘテロナノ ソシキ Cu-Beケイ ゴウキン ノ ソシキ ト リキガクテキ トクセイ

この論文をさがす

抄録

<p>Microstructures and mechanical properties of Cu–Be–Co alloys having four different Be contents and prepared by simply heavy cold rolling (CR), were systematically investigated. The cold–rolled alloys exhibited excellent mechanical properties due to the development of heterogeneous–nano (HN) structure during CR, which consists of rhombic deformation twin domains surrounded by shear bands and further embedded in conventional lamella. The strength of each alloy increased with increasing Be content. The volume fraction of twin domains in each alloy was quantitatively evaluated by texture analyses. It increased with increasing Be content rapidly from 0.40 mass% to 1.27 mass% and was gradually up to 2.14 mass%. The latter stagnation was attributed to the formation of coarse particles of intermetallic phases, which inhibited the formation of the HN structure. It revealed that the change in strength was correlated well with the volume fraction of twin domains.</p>

収録刊行物

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ