Molecular Aggregation Structure of Notched Nylon 12 Film during Uniaxial Elongation
-
- TAKAYAMA Nobuhisa
- Graduate School of Engineering, Kyushu University
-
- TAKADA Akihiko
- Institute for Materials Chemistry and Engineering, Kyushu University
-
- KOJIO Ken
- Graduate School of Engineering, Kyushu University Institute for Materials Chemistry and Engineering, Kyushu University WPI-I2CNER, Kyushu University
-
- TAKAHARA Atsushi
- Graduate School of Engineering, Kyushu University Institute for Materials Chemistry and Engineering, Kyushu University WPI-I2CNER, Kyushu University
Bibliographic Information
- Other Title
-
- ノッチを導入したナイロン12フィルムの一軸伸長過程における分子凝集構造評価
- ノッチ オ ドウニュウ シタ ナイロン 12 フィルム ノ イチジク シンチョウ カテイ ニ オケル ブンシ ギョウシュウ コウゾウ ヒョウカ
Search this article
Abstract
<p>Polarizing observation was carried out for nylon 12 (Ny12) films with a notch of ca. 0.2 mm length during uniaxial elongation. As the result, a ductile deformation behavior was detected, and a X-shaped area with higher retardation was observed around the notch extending to 45˚inclined direction to the uniaxial elongation direction. Moreover, during the uniaxial elongation, in-situ wide angled X-ray diffraction (WAXD) measurement were performed at various positions in the Ny12 film specimens. As a result, a crystal phase transition from γ-crystal to α-crystal seemed to occur in the region where higher retardations were observed. Since the intrinsic birefringence in α-crystal is higher than those in γ-crystal and amorphous phases, the increase in retardation can be caused by increase of α-crystalline fraction.</p>
Journal
-
- NIPPON GOMU KYOKAISHI
-
NIPPON GOMU KYOKAISHI 94 (9), 293-298, 2021
THE SOCIRETY OF RUBBER SCIENCE AND TECHNOLOGYY, JAPAN
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390290384176537472
-
- NII Article ID
- 130008128294
-
- NII Book ID
- AN00269207
-
- ISSN
- 18840442
- 0029022X
-
- NDL BIB ID
- 031677306
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed