切削過程に於ける摩擦係数と切屑接触率に就いて

DOI 機関リポジトリ Web Site

書誌事項

タイトル別名
  • The Relationship between the Coefficient of Friction and Contact Ratio on Cutting Process
  • セッサク カテイ ニ オケル マサツ ケイスウ ト キリクズ セッショクリツ ニ ツイテ

この論文をさがす

抄録

type:Article

Some investigators proposed that the coefficient of friction occures due to the welding action and the shearing action at the tool-chip interface and the welded film thickness would be so thin that shearing action significantly was affected with the Size effect at thus film gone. In general the coefficient of friction is expressed by terms of modulus of rigidity, flow hardness and contact ratio. In the other hand the coefficient of friction was actually measured by the axial force and the tangential force measurement at the orthogonal cutting. Then the contact ra1io, that is, fraction of actual contact area to the apparent contact area was derived from the expermental result of the modulus of rigidity, the flow hardness and the coefficient at various conditions. In this experment cutting force was measured by the strain gauge method and modulus of rigidity was derived from twisting moment measuring method and the flow hardness was measured by the author's special apparatus. From these experimental results it would be concluded that contact ratio would not be proportional to the coefficient of friction and its value would vary about O.3--O.5.

今迄の各種の実験によって切削過程に於けるバイト掬面上の摩擦係数が各種の作業条件，加熱温度，材質並びに刃物角度によって，それぞれ異なる結果を生ずることが知られる。然れども如何なる理由によってこの様に異なる結果を生ずるかは的確な論拠にとぼしい。H.BlockやK.J.Trigger等が提唱する如く，バイトと切屑との接触面は相互の無数の小凸起の接触によって構成され，切削過程に於いてはこれらの小凸起が切削力に基づく高温と高圧によって融着されてバイト面上に極めて薄い融着層を生ずる。切削過程に於ける摩擦係数はこの融着層の剪断破壊によって生ずるといわれている。従って小凸起の数の大小が摩擦係数と関連することが予想される。凸起の数が即ち接触面であり，見かけの接触面と真の接触商との比Ar/A = Kとし，これを接触率と名付けると，Kの値の大小によって摩擦係数が左右されることが推測される。本実験は各種の作業条件，材質，加熱温度並びに刃物角度がKの値や摩擦係数に如何に影響するかを究明する為めに行うものである。

identifier:富山大学工学部紀要，10(1/2), Page 108-112

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ