MgO・CaO-Fe-Si系還元反応の収率に影響する因子について

DOI 機関リポジトリ Web Site

書誌事項

タイトル別名
  • Several Factors Effect on the Yield of Reducing Reactions in MgO・CaO-Fe-Si System
  • MgO CaO-Fe-Siケイ カンゲン ハンノウ ノ シュウリツ ニ エイキョウ スル インシ ニ ツイテ

この論文をさがす

抄録

type:Article

Having studied on the effects on the yield of MgO・CaO-Fe-Si system, reducing reactions, the following results were obtained. Relations between yield (y%) an d degree of vacum (xmmHg) are shown in the following formulas: y= 82. 70-2.85 logx, y=78.98-7.20 logx. The yield for magnesium of the wet briquette shows about 5% higher than that of the dry briquette perhaps due to the decomposition of Ca(OH)_2. From the industrial view points, addition of 5 % MgO to dolomite seems to be more preferable than that of CaO for the increasing production of magnesium. Relation between velocity constant of reaction (k) and diameter of briquettes (d) is approximately represented in the equation; k=9.6 X 10^-3e ^-0.0584d Using several reducing materials, the activation energy of reducing reactions obtained as follows: MgO・CaO-Si system, 46,300 cal/mol; MgO・CaO-Fe-Si system, 55,500 cal/mol; MgO・CaO-Al-Si system, 40,300 cal/mol; MgO-Ca-Si system, 54,200 cal/mol; MgO・CaO-Al-_si-Fe system, 71,500 cal/mol; MgO-Fe-Si system, 67,200 cal/mol;

さきに還元法による金属マグネシウムの製造に関する研究において，MgO-Fe-Si系の還元では反応過程においてMg_2SiO_4が生成してMgOの相当量が未反応のままで残留することを報告した。Mg_2SiO_4の生成を抑制するためにMgO・CaoをFe-Siで還元することがPidgeonによって提唱され，その後二，三の研究が行われてはいるが，幾多の問題が未解決のまま残されている。MgO・CaO-Fe-Si系の還元反応の収率におよぼす加熱温度，時間，Fe-Siの混合割合，CaO/MgO，Al_2O_3，Fe_2O_3，SiO_2，煆焼条件，添加剤の影響などについてはさきに報告した。本報においては真空度，ブリケットの製造条件，冷却条件，MgO，CaOの添加，ブリケットの大きさ，各種の還元剤の影響などについて実験を行った結果について報告したい。

identifier:富山大学工学部紀要，14(1/2)

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ