Abstract

type:Article

Influence of mold is one of the vari ous important factors as the reason of the casting stress.For, the cooling ability, the strength, the expansion rate, and the deformation capacity of mold in hight emperature which have thermal influence when the melt in high temperature is poured into the mold, differ one another. Therefore the stress also differs in this experi ment, we studied the effects of the properties in high temperature (i.e. the strength in high temperature, thermal expansion, deformation capacity) on the casting stress. The results obtained are as follows; (1) Even if the expansi on rate is low, in case the high temperature strength is high, the free shrinkage of casting is much influenced, because the high-temperature strength prevents contraction stress from increasing. (2) Even if the high-temperature strength and the expansion rate are high, in case the deformation capacity is high, the contraction stress of casting is little influenced. (3) The deformation capacity of mold and the bond material in mold are much influenced by moisture in mold at high temperature. (4) In the case of using extremely different mold material at a part which contacts with casting the deformation of casting occurs.

鋳物の鋳造応力の原因として，鋳型の影響は，みのがすことのできない大きな因子である。鋳型の冷却能，そして高温の溶湯が注入された時，熱影響をうける鋳型の，高温での抗圧力，膨張率，可縮性などが変わり，それによって，応力もことなってくると思われるからである。本実験では，鋳型の高温抗圧力，熱膨張，変形能など高温での性質が，応力にどのような影響を与えるかについて研究した。得られた結果は，次のとおりである。 (1) 高温抗圧力が大きいものは，膨張率が小さくても，鋳物の収縮応力増加を妨げるため，鋳物の自由な収縮に大きな影響を与える。 (2) 高温抗圧力が大きく，膨張率の大きいものでも変形能が大きければ，あまり収縮応力に影響を与えない。 (3) 鋳型の変形能と，粘結剤は，高温での鋳型内の水分の挙動に大きな影響をうける。 (4) 鋳型の鋳物に接する部分の一部を，極端に異なった材料にすると，鋳物の変形をおこす。

identifier:富山大学工学部紀要，25

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top