- Electrodeposition of High-bright Hard Cr-C Layers on Steel Plate Cold-rolled Commercial from Trivalent Chromium/Organic Additives/Highly Concentrated Conductive Salt Aqueous Baths
- サンカ クロム/ユウキ テンカザイ/ノウコウ デンドウセイエン スイヨウセイヨク カラ ノ レイカン アツエン コウバン ジョウ エ ノ コウタクセイ コウシツ Cr-C デンキメッキ
この論文をさがす
抄録
<p>To prepare Cr-C alloy layers having high current efficiency, high Vickers hardness, and high brightness in electrodeposition on commercial cold-rolled steel plate, this study examined additives put into electrodeposition baths. From a Cr2 （SO4）3/（NH4）2SO4 aqueous bath containing oxalic acid and CrCl3/highly concentrated CaCl2/H3BO3 aqueous bath containing glycine, Cr-C alloy layers having high current efficiency, high Vickers hardness, and high brightness were formed. With the optimized bath compositions, the Cr-C alloy layers were produced with high current efficiency, high Vickers hardness, and high brightness. The highest current efficiency of 31.8% was obtained in a 0.4 mol kg－1 glycine/0.75 mol kg－1 CrCl3/4.68 mol kg－1 CaCl2/0.49 mol kg－1 H3BO3 bath. The Cr-C layers mainly comprised Cr3C2 and Cr7C3 alloys.</p>
収録刊行物
-
- 表面技術
-
表面技術 73 (7), 365-373, 2022-07-01
一般社団法人 表面技術協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390292936927773696
-
- NII書誌ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 032270235
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可