Effect of <i>Q</i>-switched Er:YAG laser irradiation on bonding performance to dentin surface

  • KASAKAWA Aya
    Division of Special Care Dentistry, Osaka University Dental Hospital
  • SEKINE Shinichi
    Department of Oral Health Sciences, Otemae Junior College
  • TANAKA Kenji
    Division of Special Care Dentistry, Osaka University Dental Hospital
  • MURAKAMI Jumpei
    Division of Special Care Dentistry, Osaka University Dental Hospital
  • KONDO Sota
    Graduate School of Engineering, Osaka University
  • HAZAMA Hisanao
    Graduate School of Engineering, Osaka University
  • AWAZU Kunio
    Graduate School of Engineering, Osaka University Global Center for Advanced Medical Engineering and Informatics, Osaka University Graduate School of Frontier Biosciences, Osaka University
  • AKIYAMA Shigehisa
    Division of Special Care Dentistry, Osaka University Dental Hospital

この論文をさがす

抄録

<p>The use of Q-switched erbium:yttrium-aluminum-garnet laser (Er:YAG laser), which have much less thermal effects than conventional Er:YAG lasers, has been proposed mainly in the medical field. The purpose of this study was to evaluate the bonding ability of dentin after Q-switched Er:YAG laser irradiation.The effects of dentin irradiation with Q-switched and conventional lasers were evaluated in terms of dentin morphology, roughness, hardness, elemental content, and resin bonding strength. Q-switched Er:YAG laser at average power densities of 20, 40, and 60 W/cm2 and conventional Er:YAG laser at 909 W/cm2 were used, and their performance was compared with that of the untreated group. Significant differences (p<0.05) were observed between 20 W/cm2 and the other groups in term of surface roughness and surface hardness. The resin adhesion of the 20 W/cm2 group was significantly higher than that of the other groups (p<0.05).</p>

収録刊行物

  • Dental Materials Journal

    Dental Materials Journal 41 (4), 616-623, 2022-07-25