Improvement of Corrosion Resistance of the AZ91 Magnesium Alloys with Sputtered Aluminum Layer Using Interdiffusion Treatment, Anodic Oxidation Treatment and Sealing Process
-
- Hatakeyama Masahiko
- Graduate School of Science and Engineering for Research, University of Toyama
-
- Nakano Kenichi
- Graduate School of Science and Engineering for Education, University of Toyama
-
- Yoshita Ryosuke
- Graduate School of Science and Engineering for Education, University of Toyama
-
- Nakato Daichi
- Department of Materials Design and Engineering, University of Toyama
-
- Sunada Satoshi
- Graduate School of Science and Engineering for Research, University of Toyama
-
- Nose Masateru
- Graduate School of Science and Engineering for Research, University of Toyama
この論文をさがす
抄録
<p>Magnesium alloys have low corrosion resistance due to their high chemical activity. Therefore, it is necessary to improve their corrosion resistance to use in corrosive environments. In the present study, we aimed to improve the corrosion resistance of AZ91 magnesium alloy in NaCl solution, using aluminum sputtering deposition, anodic oxidation treatment and sealing process were examined. To evaluate the corrosion rate, electrochemical experiments were carried out. In the case of just aluminum sputtering deposition, corrosion resistance was not improved due to small defects in the sputtering deposition. However, corrosion resistance was improved by sputtering deposition followed by interdiffusion treatment at 553 K for more than 3 hours. Corrosion resistance was further improved by anodic oxidation treatment and sealing process after the interdiffusion treatment. With this series of treatments, the corrosion rate of the samples was reduced to 1/360 compared to that of AZ91 base metal. The results show that the interdiffusion treatment, anodic oxidation treatment and sealing process after sputtering deposition are significantly effective to improve corrosion resistance of AZ91 magnesium alloy.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 63 (9), 1242-1247, 2022-09-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390293191189523200
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 032367073
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可