Suppression of Hydrogen Embrittlement due to Local Partitioning of Hydrogen to Dispersed Intermetallic Compound Particles in Al–Zn–Mg–Cu Alloys

DOI HANDLE Web Site Web Site 被引用文献4件 参考文献44件 オープンアクセス

この論文をさがす

説明

<p>Recent studies have revealed that hydrogen embrittlement in Al–Zn–Mg alloys appears to be dominated by hydrogen partitioning to MgZn2 precipitates. A method has recently been proposed for reducing the hydrogen concentration at MgZn2 precipitates by adding specific intermetallic compound particles that have high hydrogen trap energy. In the present study, the effectiveness of Al7Cu2Fe particles on suppression of hydrogen embrittlement in Al–Zn–Mg–Cu alloys was evaluated using X-ray microtomography. Quasi-cleavage cracks were found to be initiated in regions where local volume fractions of the Al7Cu2Fe particles were relatively low. Hydrogen partitioning to the MgZn2 precipitate interface was suppressed, even in high hydrogen concentration material, by adding Al7Cu2Fe particles. However, the fractional area of the quasi-cleavage fracture in the material with high hydrogen concentration was higher due to insufficient hydrogen diffusion inside the Al7Cu2Fe particles and at the interface between the aluminum matrix and the particles. It appears that finely distributed small Al7Cu2Fe particles might effectively suppress hydrogen embrittlement.</p>

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 63 (10), 1406-1415, 2022-10-01

    公益社団法人 日本金属学会

被引用文献 (4)*注記

もっと見る

参考文献 (44)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ