Effect of Nb Content on Microstructure and Properties of Fe–20Mn Alloy Prepared by Ball Milling and Spark Plasma Sintering
-
- Huang Lin
- School of Mechanical Engineering, Chengdu University Sichuan Province Engineering Technology Research Center of Powder Metallurgy
-
- Xiong Ke
- School of Mechanical Engineering, Chengdu University Sichuan Province Engineering Technology Research Center of Powder Metallurgy
-
- Wang Xiaofeng
- Guang’an Vocational and Technical College
-
- Yu Lin
- School of Mechanical Engineering, Chengdu University Sichuan Yiran Material Technology Co., Ltd.
-
- Feng Wei
- School of Mechanical Engineering, Chengdu University Sichuan Province Engineering Technology Research Center of Powder Metallurgy
Search this article
Abstract
<p>In this paper, Fe–20Mn–xNb alloys were prepared by ball milling and spark plasma sintering techniques. Phase constituents were characterized by X-ray diffractometer and Microstructure were characterized by scanning electron microscopy, and the tensile properties, hardness, compactness and damping properties were tested as well. The results show that after ball milling, the metal powders of Fe–20Mn–3Nb first exhibited an irregular plate-like or flake-like morphology, then large irregular particles were broken into fine particles. The addition of Nb element significantly increases the content of γ and ε phase, promoting the formation of γ and ε, and Fe2(Nb, Mn) phase precipitates in Fe–20Mn–3Nb alloy. And mechanical properties of the alloy are significantly improved by adding Nb element. The UTS and YS of Fe–20Mn–3Nb alloy are the highest, which are 818 MPa and 628.7 Mpa respectively, while the elongation of Fe–20Mn–0.5Nb alloy is the highest, which is 31.7% (20.2% higher than that of 0Nb alloy). The hardness and density of the alloy can be increased by adding Nb. The fracture mechanism of Fe–20Mn–xNb (x = 0.5, 1.5, 3) alloys is typical ductile fracture, while the fracture mechanism of Fe–20Mn alloy is quasi-xcleavage fracture. The damping property of Fe–20Mn alloys increases with increasing strain. The addition of Nb can significantly improve the damping properties of Fe–Mn alloys.</p>
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 64 (6), 1250-1256, 2023-06-01
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390296210357817856
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 032853978
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
-
- Abstract License Flag
- Disallowed