Effect of Stability of γ phase on Lüders-like Deformation Behavior of Cold-rolled Fe-Ni-Al-C Alloys

DOI Web Site 24 References Open Access

Bibliographic Information

Other Title
  • Fe-Ni-Al-C 系合金冷間圧延材のリューダース型変形挙動に及ぼすγ相安定性の影響

Description

<p>The effect of stability of austenite (γ) phase on Lüders-like deformation behavior of cold-rolled Fe-Ni-Al-C alloys was investigated by digital image correlation (DIC) analysis, magnetic measurements and electron backscatter diffraction (EBSD) analysis. In this study, cold-rolled Fe-23Ni-5.0Al-0.5C (mass%) alloy (23Ni alloy) and Fe-25Ni-5.0Al-0.5C (mass%) alloy (25Ni alloy) were used. The tensile strength increased and the total elongation decreased with decreasing Ni content. Lüders-like deformation after yielding was observed up to a nominal strain of approximately 0.04 for the 23Ni alloy and approximately 1.0 for the 25Ni alloy. The transformation from γ to martensite (α') with a specific crystal orientation relationship was observed during tensile deformation, and it was found that the volume fraction of α' during tensile deformation increased more easily in 23Ni alloy than in 25Ni alloy. In addition, the increment of α' phase in 25Ni alloy was higher during Lüders-band propagation than after the band propagation. These results suggested that change of the Lüders-like deformation behavior was due to the change in γ stability.</p>

Journal

  • Tetsu-to-Hagane

    Tetsu-to-Hagane 109 (8), 695-703, 2023-08-01

    The Iron and Steel Institute of Japan

References(24)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top