Anisotropy of Tensile and Fracture Behavior of Pure Titanium after Hydrostatic Extrusion

  • Moreno-Valle E.C.
    IMDEA Materials Institute Siemens Gamesa Renewable Energy S.A.
  • Pachla W.
    Institute of High Pressure Physics, Polish Academy of Sciences
  • Kulczyk M.
    Institute of High Pressure Physics, Polish Academy of Sciences
  • Sabirov I.
    IMDEA Materials Institute
  • Hohenwarter A.
    Department Materials Science, Chair of Materials Physics, Montanuniversität Leoben

この論文をさがす

抄録

<p>Commercially pure titanium was subjected to hydrostatic extrusion resulting in formation of an ultra-fine grained microstructure with a strong α-fiber texture and significant improvement of mechanical strength. Anisotropy of the tensile and fracture behavior of the hydrostatically extruded material was studied. It will be demonstrated that the material has significantly higher yield strength along the extrusion direction, while in transversal direction it shows higher work hardening ability related to the α-fiber crystallographic texture. The anisotropy of the fracture behavior in these two directions is less pronounced. A slightly lower fracture initiation toughness and crack growth resistance along the extrusion axis can be related to a lower crack propagation resistance along the boundaries of the elongated grains.</p>

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 60 (10), 2160-2167, 2019-10-01

    公益社団法人 日本金属学会

被引用文献 (4)*注記

もっと見る

参考文献 (41)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ