溶融SnもしくはSn-Ag合金から生成する初晶（<i>β</i>-Sn）の核生成に対するZnOの効果

DOI Web Site Web Site 参考文献28件

書誌事項

タイトル別名
  • Effect of ZnO on the Nucleation of Primary <i>β</i>-Sn in Molten Sn or Sn-Ag Alloy
  • 溶融SnもしくはSn-Ag合金から生成する初晶(β-Sn)の核生成に対するZnOの効果
  • ヨウユウ Sn モシクワ Sn-Ag ゴウキン カラ セイセイ スル ハツショウ(v-Sn)ノ カク セイセイ ニ タイスル ZnO ノ コウカ

この論文をさがす

抄録

<p>The amount of undercooling required for the nucleation of (β-Sn) in Sn-6.0 mass%Zn alloy was found to be extraordinarily small compared with other Sn-based alloys. One reason for this may be that the solute Zn is oxidized during the process to form ZnO, and this may assist the nucleation of (β-Sn). The disregistry between ZnO and (β-Sn) was analyzed. It was found that crystalline ZnO may be effective for nucleation of (β-Sn), since the disregistry is small. In order to test the nucleation effect of ZnO on β-Sn, dipping experiments were carried out. ZnO powder used in this study was analyzed by X-ray and found to be crystalline. Pure Sn and Sn-2 mass%Ag alloy were chosen as test metals and the undercooling for nucleation of (β-Sn), ΔT, was characterized. It was found that ΔT was large regardless of whether ZnO was dipped in the Sn alloy melt. This indicates that ZnO may not be effective for the nucleation of (β-Sn). Therefore, it can be concluded that low disregistry is a necessary condition but does not ensure nucleation.</p>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 82 (6), 204-212, 2018-06-01

    公益社団法人 日本金属学会