熱水環境における天青石の炭酸塩化:炭酸水素ナトリウム溶液を用いた実験

書誌事項

タイトル別名
  • Carbonation of celestine under hydrothermal condition: an experiment with sodium bicarbonate solution
  • ネッスイ カンキョウ ニ オケル テンセイセキ ノ タンサン エンカ : タンサン スイソ ナトリウム ヨウエキ オ モチイタ ジッケン

この論文をさがす

抄録

In order to understand the processes and mechanism for the formation of strontianite from celestine under the existence of bicarbonate, chemical reaction of celestine with sodium bicarbonate solution was experimentally examined. Natural celestine grains between 1.00 and 1.18 mm in diameter were sealed in the teflon bottle which contains aqueous NaHCO3 solution. A series of experiment with 1/900 mineral/solution weight ratio was carried out with changing temperature (100, 125 and 150°C), initial NaHCO3 concentration (0.01, 0.05, 0.10, 0.50 and 1.00 mol/l), and reaction time (2, 4, 8, 12, 24 and 96 hours). The run products were filtered by 0.20 μm membrane filters, and the filtrate and residual solid were analyzed. In addition, a series of experiment with 1/450 mineral/solution weight ratio with celestine grains between 2.36 and 4.75 mm in diameter was also carried out for observation of solid profiles.<br>Regardless of the various conditions, the only identified reaction product was strontianite, which is well correlated with the equilibrium calculation results. Amount of strontianite relative to celestine increases with the increase in temperature, initial NaHCO3 concentration and reaction time, in the range of ~0% for the condition of initial NaHCO3 0.01 mol/l-100°C-2 hours and 90.0% for 1mol/l-150°C-96 hours. Strontianite develops as aggregates or layers of crystals on the surface of initial celestine grains. The depth of strontianite layer increases with the increase in reaction time, suggesting that the reaction occurs at the interface between solid and solution. The crystal habits of strontianite on the surface differ with the initial NaHCO3 concentration: granular, platy and bladed crystals with cauliflower-like aggregates in increasing order. The rate of strontianite formation from celestine for 24 hours increases with the increase of temperature and initial NaHCO3 concentration, in the range of 2.95x 10-6 mol·s-1·m-2 for the condition of initial NaHCO3 0.01 mol/l-100°C and 6.88 x 10-5 mol·s-1·m-2 for 1.00 mol/l-150°C. Thus, formation of strontianite from celestine proceeds under the existence of bicarbonate even at low temperature.

収録刊行物

  • 資源地質

    資源地質 65 (1), 13-22, 2015

    資源地質学会

関連プロジェクト

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ