Structure and Magnetic Properties of Co–Ni Spinel Ferrite Particles Synthesized via Co-Precipitation and Hydrothermal Treatment at Different Temperatures
-
- Kishimoto Mikio
- Institute of Applied Physics, University of Tsukuba
-
- Latiff Hawa
- Institute of Applied Physics, University of Tsukuba
-
- Kita Eiji
- Institute of Applied Physics, University of Tsukuba
-
- Yanagihara Hideto
- Institute of Applied Physics, University of Tsukuba
この論文をさがす
抄録
<p>Co–Ni spinel ferrite particles were synthesized via chemical co-precipitation and subsequently performed hydrothermal treatment at different temperatures. Fine particles of size with a few nanometers and spherical or cubic particles of size approximately 30 nm, which are responsible for magnetic properties, were obtained. The crystallite size obtained using the Scherrer equation was 24–27 nm and showed no dependency on the hydrothermal treatment temperature unlike the apparent particle size observed using transmission electron microscopy. The coercive force showed a remarkable increase with the decrease in the hydrothermal treatment temperature from 141 kA/m at 240°C to 400 kA/m at 100–120°C, in contrast to the decrease in magnetization from 60.0 Am2/kg at 240°C to 37.2 Am2/kg at 100°C. The specific composition of the Co–Ni spinel ferrite particles is expected to affect the high coercive force and the remarkable dependency of the coercive force on the hydrothermal treatment temperature.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 60 (4), 485-489, 2019-04-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390564238092873088
-
- NII論文ID
- 40021860598
- 130007618549
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 029620890
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可