Tensile Behavior and Superplastic Deformation of Sn–Bi–Cu Alloy
-
- Umeyama Junpei
- Department of Mechanical Engineering, National Institute of Technology, Gunma College
-
- Yamauchi Akira
- Department of Mechanical Engineering, National Institute of Technology, Gunma College
Search this article
Description
<p>The purpose of this study is to clarify the tensile behavior and deformation mechanism of the Sn–40Bi–0.1Cu alloy (mass%). Tensile tests of Sn–40Bi–0.1Cu were performed at temperatures of 298, 333, and 353 K and strain rates from 5.25 × 10−5 to 5.25 × 10−2 s−1. The tensile strength decreased and the elongation increased with increasing temperature and decreasing strain rate. Sn–40Bi–0.1Cu shows superplastic behavior at temperatures of >333 K and low strain rates of <5.25 × 10−4 s−1. Microstructural observation after superplastic deformation of Sn–40Bi–0.1Cu showed that the primary crystal Sn grains could not deform along the axial direction of applied tension in the superplastic regime. The eutectic phase contributed to superplastic deformation. The strain rate sensitivity m for Sn–40Bi–0.1Cu was <0.3.</p>
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 60 (6), 882-887, 2019-06-01
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390564238094113536
-
- NII Article ID
- 130007653204
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 029707015
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed