- Change in microstructures and mechanical properties during annealing of AZ31F magnesium alloy multi-directionally forged under decreasing temperature conditions
- コウオン タジク タンゾウ シタ AZ31Fマグネシウム ゴウキン ノ ヤキ ナマシ ニ オケル ビシ ソシキ オヨビ キカイテキ セイシツ ノ ヘンカ
この論文をさがす
抄録
<p>Hot extruded AZ31F magnesium alloy was multi-directionally forged (MDFed) to 6 passes (a cumulative strain of ΣΔε=4.8) under decreasing temperature conditions, and then the specimens MDFed to 6 passes were annealed at temperatures ranging from 373 to 623 K. The as-MDFed specimen possessed a weak (0001) texture, whereas the MDFed specimen annealed at 623 K almost random orientation. Average grain size and hardness before and after static recrystallization indicated 0.6 µm and 85.1Hv, and 3.2 µm and 58.5Hv, respectively. The relationship between hardness (Hv) and grain size (d) in both as-MDFed and as-annealed specimens followed the Hall–Petch relation, which was expressed by a unified equation of Hv=38.7+36d −1/2。</p>
収録刊行物
-
- 軽金属
-
軽金属 69 (4), 228-234, 2019-04-30
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390564238096266368
-
- NII論文ID
- 130007655570
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 029658503
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可