Deposition-Temperature Dependence of Vortex Pinning Property in YBa₂Cu₃O₇+BaHfO₃ Films

DOI 機関リポジトリ HANDLE Web Site Web Site 被引用文献1件 参考文献20件 オープンアクセス
  • Horide Tomoya
    Department of Materials Science and Engineering, Kyushu Institute of Technology
  • Torigoe Kenta
    Department of Materials Science and Engineering, Kyushu Institute of Technology
  • Kita Ryusuke
    Graduate School of Integrated Science and Technology, Shizuoka University
  • Nakamura Ryota
    Department of Materials Science and Engineering, Kyushu Institute of Technology
  • Ishimaru Manabu
    Department of Materials Science and Engineering, Kyushu Institute of Technology
  • Awaji Satoshi
    Institute for Materials Research, Tohoku University
  • Matsumoto Kaname
    Department of Materials Science and Engineering, Kyushu Institute of Technology

書誌事項

タイトル別名
  • Deposition-Temperature Dependence of Vortex Pinning Property in YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7</sub>+BaHfO<sub>3</sub> Films

この論文をさがす

抄録

<p>Improvement of critical current density (Jc) in magnetic fields is required in YBa2Cu3O7 films, and process parameters should be optimized for controlling pinning centers. In the present study, a deposition temperature was varied in pulsed laser deposition of YBa2Cu3O7+BaHfO3 films to control the nanorod structure, and its influence on Jc was analyzed. The YBa2Cu3O7+BaHfO3 film deposited at 850°C exhibited pinning force maximum (Fp,max) as high as 413 GN/m3 at 40 K, while the Fp,max for the deposition temperature of 850°C at 77 K was smaller than that in the YBa2Cu3O7+BaHfO3 film deposited at 900°C. A critical temperature decreased and matching field increased with decreasing the deposition temperature. Increase in deposition temperature is effective in improving the Fp,max in high temperatures, since the critical temperature and matching field dependences of Jc value dominate the Fp,max. On the other hand, low deposition temperature improves the Fp,max in low temperatures since the Fp shift in accordance with matching field is dominant to the Fp,max. Thus, the deposition temperature should be set in pulsed laser deposition of YBa2Cu3O7 films containing nanorods considering the Jc variation with critical temperature and matching field.</p><p> </p><p>This Paper was Originally Published in Japanese in J. Japan Inst. Met. Mater. 83 (2019) 320–326.</p>

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 61 (3), 449-454, 2020-03-01

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (20)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ