- Microstructure and Mechanical Properties of Multi-Directionally-Forged AZ80-F Magnesium Alloys at Warm Temperatures
- オン カン タジク タンゾウ AZ80-Fマグネシウム ゴウキン ノ ソシキ ト キカイテキ セイシツ
この論文をさがす
抄録
<p>A hot extruded AZ80-F magnesium alloy was multi-directionally forged (MDFed) up to a cumulative strain of ΣΔε = 2.4 at warm temperatures of 543 K, 573 K and 593 K. Fine grained structures were gradually developed with increasing cumulative strain due to extensive occurrence of dynamic recrystallization. Bimodal grain size distribution tended to appear when MDFed to lower cumulative strain and/or at lower temperatures. The yield stress of the MDFed AZ80-F alloys with homogeneous grain size distribution followed the Hall-Petch relationship. MDFing to ΣΔε = 2.4 at 543 K exhibited the most excellent balance of mechanical properties of 260 MPa yield stress, 347 MPa tensile strength and 24% elongation to fracture. The warm MDFed Mg alloys accepted additional 10% cold rolling to cause further strengthening by strain hardening and sharp basal texture evolution.</p>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 84 (6), 190-199, 2020-06-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390566775135839360
-
- NII論文ID
- 130007846049
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 030474373
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可