Cu–Be–Co合金の強度に及ぼす強圧延ヘテロナノ組織の影響

DOI Web Site 被引用文献3件 オープンアクセス

書誌事項

タイトル別名
  • Influence of Heavily Rolled Heterogeneous Nano–Structure on Strength of Cu–Be–Co Alloys
  • Cu-Be-Co ゴウキン ノ キョウド ニ オヨボス キョウアツエン ヘテロナノ ソシキ ノ エイキョウ

この論文をさがす

抄録

<p>Heterogeneous–nano （HN） structures induced by heavy cold rolling of Cu–Be–Co alloys and their influence on the mechanical properties were systematically investigated to develop thermo–mechanical process applicable to the industrial mass–production. The HN–structure was successfully developed by the combination of differential speed cold rolling and simple cold rolling with the reduction up to 97％ at maximum after the solution–annealing between 850 and 867°C. The HN structure possessed characteristic eye–shaped domains consisting of alternatively stacked deformation twin bands. Aging at 285°C of the HN structured Cu–1.86mass％Be–0.23mass％Co alloy caused a marvelous tensile strength of 1.78 GPa, which was significantly higher than that of 1.3 GPa of a conventional Cu–Be–Co alloy （C17200） fabricated by conventional thermo–mechanical processes. It was also shown that the developed HN structured Cu–Be–Co alloy exhibited comparable bending formability and electrical conductivity with those of the conventional one. While, in contrast, the fatigue strength was slightly lower than that of the conventional one. It is confirmed that introduction of HN structured Cu–Be–Co alloys can be fabricated by means of a newly developed thermo–mechanical process applicable to the industrial–scale mass production.</p>

収録刊行物

被引用文献 (3)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ