- Fabrication of CuO nanowire synthesized by thermal oxidation and influence of the fabrication conditions on capacitance of supercapacitor electrode
抄録
<p>Some nanostructures using a transition metal oxide such as CuO, which is attracting attention as a pseudo-capacitive material, is applied to the electrode surface. In this research, one of the nanostructures, CuO nanowire was synthesized by thermal oxidation method. In addition, influence of the fabrication conditions on capacitance of supercapacitor electrode was investigated. In order to investigate the influence, morphological observation, wettability evaluation, and cyclic voltammetry were conducted for the CuO nanowire specimen. As a result, depending on the production conditions, differences were observed both in the wettability of the specimen surface and in the results of cyclic voltammetry. The surface of the CuO nanowire specimen heated for 6 and 8 hours showed hydrophilicity, on the other hand that heated for 2 and 4 hours showed hydrophobicity. Only the specimen heated for 6 hours with hydrophilicity showed good electrochemical properties. Consequently, it became clear that the conditions for synthesized the test piece by the thermal oxidation method affect the wettability of the test piece surface which affects the performance of the supercapacitor electrode.</p>
収録刊行物
-
- 日本機械学会関東支部総会講演会講演論文集
-
日本機械学会関東支部総会講演会講演論文集 2020 (0), 17I14-, 2020-03-13
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390568772520707840
-
- NII論文ID
- 130007994554
-
- ISSN
- 24242691
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可