ワット浴からの低熱膨張型Fe-Niインバー合金の電析挙動と微細構造に及ぼす添加剤の影響

DOI DOI 機関リポジトリ 機関リポジトリ (HANDLE) Web Site ほか2件をすべて表示 一部だけ表示 被引用文献3件 参考文献30件 オープンアクセス

書誌事項

タイトル別名
  • Effect of Additives on the Deposition Behavior and Micro Structure of Invar Fe-Ni Alloys with Low Thermal Expansion Electrodeposited from Watt’s Solution
  • ワットヨク カラ ノ テイネツ ボウチョウガタ Fe-Ni インバー ゴウキン ノ デンセキキョドウ ト ビサイ コウゾウ ニ オヨボス テンカザイ ノ エイキョウ

この論文をさがす

説明

<p>The electrodeposition of invar Fe-Ni alloy with low thermal expansion was performed at 100-5000 A·m–2 and 105 C·m–2 in agitated Watt’s solution containing NiSO4, NiCl2, FeSO4, C3H4O4, C7H4NNaO3S and H3BO3 at 50ºC. With increasing the concentration of malonic acid, the Ni content in deposits decreased at higher current density region than 2000 A·m–2, while it increased at lower current density region than 1000 A·m–2. The current efficiency for alloy deposition decreased with increasing the concentration of malonic acid. The deposits were composed of granular crystals whose size decreased with increasing the concentration of malonic acid. With an addition of saccharin, the Ni content in deposits significantly decreased, and the current efficiency for alloy deposition increased. With an addition of boric acid, the Ni content in deposits somewhat decreased, and the current efficiency for alloy deposition increased. The surface morphology of deposits changed with the current density and an addition of saccharin, and rarely changed with an addition of boric acid. It was found that the morphology depended on the Ni content in deposits. The deposits with Ni content of 29-38 mass% were composed of granular crystals approximately 300 nm in size, while the deposits with Ni content of 41-52 mass% showed the smooth surface consisted of fine crystals. The effects of additives on the Ni content in deposits and current efficiency can be explained by the change of partial polarization curve for Fe and Ni deposition and hydrogen evolution in Fe-Ni alloy deposition.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 105 (10), 988-997, 2019

    一般社団法人 日本鉄鋼協会

被引用文献 (3)*注記

もっと見る

参考文献 (30)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ