第一原理計算と結晶方位解析を用いたC14 Fe<sub>2</sub>W Laves相の劈開破壊挙動の評価

DOI Web Site Web Site 参考文献44件

書誌事項

タイトル別名
  • Evaluation of Cleavage Fracture Behavior of C14 Fe<sub>2</sub>W Laves Phase by First Principle Calculation and Crystal Orientation Analysis
  • 第一原理計算と結晶方位解析を用いたC14 Fe₂W Laves相の劈開破壊挙動の評価
  • ダイイチ ゲンリ ケイサン ト ケッショウ ホウイ カイセキ オ モチイタ C14 Fe ₂ W Lavesソウ ノ ヘキカイハカイ キョドウ ノ ヒョウカ

この論文をさがす

抄録

<p>Cleavage fracture of C14 Fe2W Laves phase was investigated using crystal orientation measurement with scanning electron microscopy and first-principles calculations. Trace analysis of the orientations of cleavage planes reveals that cleavage fracture occurred at five types of crystal planes of (0001), {1100}, {1120}, {1101} and {1122}, among which the fracture at (0001) is the most preferable. The first-principle calculations of the surface energy for fracture, Young's modulus, and Poisson's ratio showed that the minimum fracture toughness value of 1.62 MPa·m1/2 was obtained at (0001). The tendency that the values of calculated fracture toughness become larger with the higher indexed planes is almost the same as the frequency of the types of cleavage planes in the trace analysis. It is concluded that the fracture toughness of C14 Fe2W Laves phase is controlled by the surface energy for fracture and Young’s modulus.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 advpub (0), 977-985, 2021

    一般社団法人 日本鉄鋼協会

参考文献 (44)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ