建築設備における硬質ポリ塩化ビニル管のソルベントクラック発生に及ぼす諸因子の基礎的調査

DOI Web Site Web Site 参考文献8件

書誌事項

タイトル別名
  • Fundamental Investigation of Various Factors Affecting the Occurrence of Solvent Cracking for Unplasticized Poly Vinyl Chloride Pipes in Building Equipment
  • ケンチク セツビ ニ オケル コウシツ ポリ エンカ ビニルカン ノ ソルベントクラック ハッセイ ニ オヨボス ショ インシ ノ キソテキ チョウサ

この論文をさがす

説明

<p>We investigated the occurrence of solvent cracking in unplasticized poly vinyl chloride pipes by preparing test materials based on the conventional method. As a results, it was confirmed that voids were occured on the inner surface of the pipe at holding time of 2 weeks under the conditions of room temperature (298 K), adhesive application amount 1.0 g and, U-band tightening torque 4 N/m. These voids were occurred linearly in the circumferential direction at the part in contact with the U-band and linearly in the axial direction at the part not in contact with the support materials. Tetrahidrofuran (THF) and 2-butane, and cyclohexanone were detected as a result of analysis of the void generation part on the inner surface of the pipe and the residual gas in the pipe. At these results, it is considered that the stress generated by the tightening of the U-band and the environmental agents THF, 2-butane, and cyclohexanone affected the void generation. Furthermore, the results of the stress analysis simulation of the U-band fixed portion showed that the tensile stress was in the part on contact with U-band and compressive stress was in the part not on contact with the support material. It was considered that the difference in these stresses and the regularity of the molecular arrangement during pipes manufacturing influence the direction of void generation. Such voids were considered to progress into cracks.</p>

収録刊行物

  • 材料

    材料 70 (8), 623-627, 2021-08-15

    公益社団法人 日本材料学会

参考文献 (8)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ