- Effect of Amount of Solute Atoms on Development of Heterogeneous–nano Structure in Cu–Ni–Si Alloys
- Cu-Ni-Siケイ ゴウキン ノ ヘテロナノ ソシキ ノ ハッタツ ニ オヨボス ヨウシツ ゲンシ テンカリョウ ノ エイキョウ
この論文をさがす
抄録
<p>The effects of amount of solute atoms on the formation of heterogeneous–nano structure in Cu–Ni–Si system alloys was investigated using Cu–2.01mass%Ni–0.44mass%Si, Cu–3.03mass%Ni–0.65mass%Si, Cu–3.60mass%Ni–0.77mass%Si, and Cu–4.2mass%Ni–0.91mass%Si alloys. All the alloys were subjected to solution–treatment and subsequent cold–rolling up to a reduction of 90% in thickness. In each alloy, conventional lamellae parallel to the rolling direction were formed after cold rolling. As the Ni and Si contents increased, in addition to the lamellae, shear bands with an angle to the rolling direction and deformation twin domains surrounded by the shear bands were formed, eventually leading to the development of distinct heterogeneous–nano structure. The Cu–4.2mass%Ni–0.91mass%Si alloy after the cold rolling was aged at 450°C for 5 min, and an excellent tensile strength of 964 MPa was achieved.</p>
収録刊行物
-
- 銅と銅合金
-
銅と銅合金 60 (1), 41-44, 2021
日本銅学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390571563558730752
-
- NII論文ID
- 130008117382
-
- NII書誌ID
- AA11995570
-
- ISSN
- 2435872X
- 13477234
-
- NDL書誌ID
- 031636668
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用可