Institute for Rural Engineering, NARO constructed several experimental ponds to evaluate the durability of waterproofing geomembrane sheet and has performed various physical property tests. In this study, tensile strength, elongation at break and tear strength of three kinds of geomembranes, which have been exposed at experimental ponds, were obtained and the tendency of deterioration was grasped. In a geomembrane mainly composed of thermoplastic resin exposed for 18 years, test pieces were sampled from part above waterline. The longitudinal tensile strength decreased to about 60% of the initial value, while the other physical properties have been kept 80% or more. On the other geomembranes mainly composed of vulcanized rubber exposed for 30 years, the tensile strength and elongation at break decreased to about 80% and 40%, respectively, while the tear strength increased to 120%. This trend was striking in the part above the waterline, compared with the part at the waterline and underwater. The elongation at break showed a clear tendency to decrease with the passage of time, so the elongation at break is the important index for diagnosing degradation of the geomembrane.

農村工学研究部門は，様々な材質の遮水シートの耐久性を評価するための実験池を築造・管理し，各種の物性試験を実施している。本研究では，実験池にて曝露された 3 種類の遮水シートの引張強さ，破断時伸び，引裂強さなどを求め，劣化の傾向を把握した。18 年間曝露された熱可塑性樹脂を主成分とする遮水シートでは，気中の長手方向の引張強さが約 60％にまで低下したが，その他の物性は 80%以上の保持率を示した。一方，30 年間曝露された加硫ゴムを主成分とする 2 種類の遮水シートは，気中ではいずれも引張強さは約 80%，破断時伸びは約 40%にまで低下するとともに，引裂強さは約 120%に上昇した。この傾向は，喫水，水中と比較して気中で最も進行していた。破断時伸びは， 時間の経過とともに低下する傾向が明瞭であり，遮水シートの劣化を診断する上で重要な指標となり得る。

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ