1073 KにおけるFe-20Cr-35Ni (at%)合金の水蒸気酸化挙動に及ぼすW添加の影響

書誌事項

タイトル別名
  • The Effect of Tungsten Addition on Steam Oxidation Behavior of the Fe-20Cr-35Ni (at%) Alloy at 1073 K

抄録

<p>This paper focuses on the effect of tungsten addition on the steam oxidation behavior of the Fe-20Cr-35Ni (at%) alloy at 1073 K. Steam oxidation tests of the W added Fe-20Cr-35Ni (at%) alloy were carried out at 1073 K in an Ar-15%H2O gas mixture for up to 604.8 ks. The oxidation resistance of the alloys was improved by adding W into the alloy. There are two effects of W on the steam oxidation behavior: the effect of solid solution and the effect of precipitation. Tungsten in the alloy is enriched as a Ni-W alloy in the matrix of the internal oxidation zone (IOZ) during oxidation. The Ni-W alloy in the IOZ may act as a diffusion barrier for oxygen and promote a continuous Cr2O3 layer. On the other hand, Fe2W precipitated in the alloy decomposes during oxidation and provides alloying elements for forming FeCr2O4 and CrWO4 in the IOZ, resulting in a continuous Cr2O3 layer formation.</p>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 86 (7), 121-130, 2022-07-01

    公益社団法人 日本金属学会

参考文献 (17)*注記

もっと見る

関連プロジェクト

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ