The Effect of Tungsten Addition on Steam Oxidation Behavior of the Fe-20Cr-35Ni (at%) Alloy at 1073 K
-
- Ogawahara Kaito
- Department of Materials Science and Engineering, School of Materials and Chemical Technology, Tokyo Institute of Technology
-
- Ueda Mitsutoshi
- Department of Materials Science and Engineering, School of Materials and Chemical Technology, Tokyo Institute of Technology
Bibliographic Information
- Other Title
-
- 1073 KにおけるFe-20Cr-35Ni (at%)合金の水蒸気酸化挙動に及ぼすW添加の影響
Abstract
<p>This paper focuses on the effect of tungsten addition on the steam oxidation behavior of the Fe-20Cr-35Ni (at%) alloy at 1073 K. Steam oxidation tests of the W added Fe-20Cr-35Ni (at%) alloy were carried out at 1073 K in an Ar-15%H2O gas mixture for up to 604.8 ks. The oxidation resistance of the alloys was improved by adding W into the alloy. There are two effects of W on the steam oxidation behavior: the effect of solid solution and the effect of precipitation. Tungsten in the alloy is enriched as a Ni-W alloy in the matrix of the internal oxidation zone (IOZ) during oxidation. The Ni-W alloy in the IOZ may act as a diffusion barrier for oxygen and promote a continuous Cr2O3 layer. On the other hand, Fe2W precipitated in the alloy decomposes during oxidation and provides alloying elements for forming FeCr2O4 and CrWO4 in the IOZ, resulting in a continuous Cr2O3 layer formation.</p>
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 86 (7), 121-130, 2022-07-01
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390574036153997312
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- KAKEN
-
- Abstract License Flag
- Disallowed