Amorphous Phase Formation in the Zirconium-Poor Corner of (Fe, Co, Ni)-Zr systems

DOI 機関リポジトリ 機関リポジトリ (HANDLE)

この論文をさがす

説明

The formation of amorphous phase was found in the limited region around 10 at% zirconium in (Fe, Co, Ni)-Zr systems. Their Vickers hardness and fracture strength were of the order of about 550-700 DPN and 1700-2100 MPa, respectively. They also were crystallized on heating at about 340-500℃ and remained ductile until the crystallization temperature.