ジンケート浴からのZn-Ni合金電析挙動に及ぼす光沢剤と浴温の相乗作用

DOI DOI 機関リポジトリ (HANDLE) Web Site Web Site 被引用文献4件 参考文献39件 オープンアクセス

書誌事項

タイトル別名
  • Synergistic Effect of Brightener and Solution Temperature on the Electrodeposition Behavior of Zn-Ni Alloy from Alkaline Zincate Solution

この論文をさがす

説明

<p>Zn–Ni alloys were electrodeposited on a Cu electrode at 10–5000 A·m−2, 5 × 104 C·m−2, and 293, 313 and 333 K in unagitated zincate solutions containing the reaction product of epichlorohydrin and imidazole (IME) as a brightener. The synergistic effect of IEM and solution temperature on the deposition behavior of Zn–Ni alloy was investigated. The transition current density, at which the deposition behavior shifted from the normal type to anomalous ones, decreased with IME at 293 K, but didn’t change regardless of IME addition at 313 and 333 K. The suppression effect of IME on the Zn and Ni depositions during alloy deposition was observed at 293 K, while at 313 and 333 K, the suppression effect was decreased on the Zn deposition but was maintained on the Ni deposition. Therefore, Ni content in deposits significantly decreased with IME as temperature increased. The current efficiency for Zn deposition significantly decreased with IME at 293 K, while the degree of decrease was small at 313 and 333 K. The content of C in deposits was highest at 293 K, and decreased with increasing solution temperature, indicating that the adsorption ability of IME on the cathode decreases with increasing temperature. As a result, the suppression effect of IME on the Zn deposition seems to decrease with increasing temperature. The gloss of deposited films was highest at 293 K. This is attributed to adsorption ability of IME being large at 293 K and deposited films with fine crystals becoming smooth.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 108 (4), 268-281, 2022

    一般社団法人 日本鉄鋼協会

被引用文献 (4)*注記

もっと見る

参考文献 (39)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ