Three Dimensional Printing of Solid Electrolyte Dendrites with Ordered Porous Structures for Fuel Cell Miniaturizations

DOI HANDLE オープンアクセス

この論文をさがす

抄録

Solid electrolyte dendrites of yttria stabilized zirconia with spatially ordered porous structures were successfully fabricated for fuel cell miniaturizations by using a micro patterning stereolithography and three dimensional printing. Micrometer order ceramic lattices with the coordination numbers 4, 6, 8 and 12 were propagated spatially in computer graphic space. Aspect ratios of the lattice diameters and lengths were designed between 1.0 and 2.0 to value the porosities in higher levels from 50 to 80 %. On the fabrication process, nanometer sized yttria stabilized zirconia were dispersed in photo sensitive liquid resins at 30 % in volume fraction to obtain thixotropic slurries. The paste material was spread on a glass substrate with 10μm layer thickness by using mechanical knife edge movements, and an ultra violet micro pattern was exposed on the surface to create a cross sectional solid layer with 2μm in part accuracy. After the layer stacking process, the ceramic dispersed resin lattices of 100μm in diameter were obtained exactly. These composite precursors were dewaxed and sintered at 600 and 1500 ºC in an air atmosphere, respectively, and fine ceramic lattices of 98 % in relative density were created. Gaseous fluid profiles and pressure distributions in the formed ceramic lattices with the various coordination numbers and porosity percents were visualized and analyzed by using a finite element method. The fabricated solid electrolytes with the extremely high porosities and wide surface areas are expected to be applied to novel electrodes in compact fuel cells. The smart processing of the solid electrolytes by utilizing computer aided design, manufacturing and evaluation methods will be demonstrated.

収録刊行物

キーワード

詳細情報 詳細情報について

  • CRID
    1390575727755397120
  • NII論文ID
    120005411577
  • NII書誌ID
    AA00867058
  • DOI
    10.18910/27404
  • HANDLE
    11094/27404
  • ISSN
    03874508
  • 本文言語コード
    en
  • データソース種別
    • JaLC
    • IRDB
    • CiNii Articles

問題の指摘

ページトップへ