CHARACTERIZATION OF C-A-S-H GEL FORMED IN C-A-S-H/N-A-S-H GEL BLENDS
-
- KAMIMURA Koya
- NIIGATA UNIVERSITY, Graduate School of Science and Technology(8050, Ikarashi, Nino-cho, Nishi-ku, Niigata-shi, Niigata 950-2181, Japan)
-
- SAITO Tsuyoshi
- NIIGATA UNIVERSITY, Faculty of Engineering(8050, Ikarashi, Nino-cho, Nishi-ku, Niigata-shi, Niigata 950-2181, Japan)
-
- SUZUKI Kazuho
- NIIGATA UNIVERSITY, Graduate School of Science and Technology(8050, Ikarashi, Nino-cho, Nishi-ku, Niigata-shi, Niigata 950-2181, Japan)
-
- SAEKI Tatsuhiko
- NIIGATA UNIVERSITY, Faculty of Engineering(8050, Ikarashi, Nino-cho, Nishi-ku, Niigata-shi, Niigata 950-2181, Japan)
Bibliographic Information
- Other Title
-
- C-A-S-Hとゼオライトの混相中におけるC-A-S-H生成領域の評価
Abstract
<p>This paper reports on the phase transformation of C-A-S-H/N-A-S-H blends and the structural characterization of C-A-S-H and zeolites formed in this process. C-A-S-H/N-A-S-H blend gels were prepared with different Si/Al and Ca/Si ratios and characterized by X-ray diffraction (XRD), fourier transform infrared spectroscopy (FT-IR) and magic angle spinning nuclear magnetic resonance (MAS NMR). The results showed that when the Al content in the blend gels was high, zeolite with a high Si/Al composition ratio is formed, and when Ca is added, C-A-S-H is formed immediately after gel mixing, but then the zeolite phase is gradually formed. On the other hand, when Al content in the blend gel was low, C-A-S-H became the main phase even with a small addition of Ca. Furthermore, FT-IR spectra may provide insight into the formation behavior of C-A-S-H and the relationship between the Ca/Si ratio and the amount of Al in solid solution in C-A-S-H.</p>
Journal
-
- Cement Science and Concrete Technology
-
Cement Science and Concrete Technology 76 (1), 485-493, 2023-03-31
Japan Cement Association
- Tweet
Details 詳細情報について
-
- CRID
- 1390577078290894720
-
- ISSN
- 21873313
- 09163182
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
-
- Abstract License Flag
- Disallowed