- Sun Hao
- Key Laboratory of Lightweight Structural Materials Liaoning Province, Northeastern University
-
- Zhao Zhanyong
- School of Materials Science and Engineering, North University of China
-
- Wang Zhi
- School of Materials Science and Engineering, Shenyang University of Technology
-
- Li Weirong
- Engineering Research Center of Continuous Extrusion, Dalian Jiaotong University Dongguan EONTEC Co. Ltd.
-
- Yu Jiangwei
- Key Laboratory of Lightweight Structural Materials Liaoning Province, Northeastern University
-
- Gao Fei
- Key Laboratory of Lightweight Structural Materials Liaoning Province, Northeastern University
-
- Cai Minghui
- Key Laboratory of Lightweight Structural Materials Liaoning Province, Northeastern University
-
- Li Yanfang
- Engineering Research Center of Continuous Extrusion, Dalian Jiaotong University
-
- Iskandarovich Giyasov S.
- Department of Urology, Tashkent Medical Academy
-
- Tie Di
- Engineering Research Center of Continuous Extrusion, Dalian Jiaotong University Dongguan EONTEC Co. Ltd.
この論文をさがす
抄録
<p>An as-cast Mg–6Zn–0.9Zr–0.9Nd (mass%) alloy was isothermally heat treated to form semi-solid microstructure, and its corrosion behaviors before and after heat treatment were revealed. During the isothermal heat treatment, the microstructure transformed into homogenous spheroidized structure, and the liquid phase presented network-shaped morphology. The electrochemical results showed that there is no passivation behavior and obvious local corrosion in the semi-solid formed alloy, and homogeneous general corrosion is the primary corrosion form. The network-shaped liquid phase prevented the flow of corrosion media between solid phases, and therefore inhibited the formation of pitting corrosion.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 64 (12), 2845-2848, 2023-12-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390579753342875776
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 033193594
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可