Texture Development in Austenite during Tensile Deformation of 5%Mn Steel Accompanied by Deformation-Induced Martensite Transformation
-
- Onuki Yusuke
- Department of Advanced Machinery Engineering, School of Engineering, Tokyo Denki University
Bibliographic Information
- Other Title
-
- 5%Mn鋼の加工誘起マルテンサイト変態に伴う引張変形中のオーステナイトの集合組織変化
Abstract
<p>Medium manganese steels, containing 3~10 mass% of Mn, are considered promising as the 3rd generation high strength steel. In this study, in situ neutron diffraction experiments were conducted during uniaxial tensile deformation for Fe-4.91Mn-0.092C (mass%). The primary aim was to investigate the change of austenite texture accompanied with the deformation induced martensitic transformation (DIMT). It was observed that grains oriented <001> towards the tensile direction tend to persist during the deformation. Moreover, the fraction of <001> oriented grains increases due to crystal rotation caused by dislocation slip. Grains with <111> towards the tensile direction are consumed more rapidly than those with <001>. These observations are qualitatively reproduced by visco-plastic self-consistent model, additionally considering DIMT to ε martensite. Although ε martensite was not identified in the diffraction pattern obtained in this study, a previous microstructural study indicated the γ→ε→α’ type DIMT for the same material. In contrast, it is known that in low alloyed TRIP steels subjected to tensile deformation, grains with <111> tend to survive, where γ→α’ type DIMT occurs. Based on the results of this study, the orientation that persists after tensile deformation can distinguish between the DIMT mechanisms: γ→ε→α’ or γ→α’ type.</p>
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 110 (3), 252-259, 2024-02-15
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390580626907726976
-
- ISSN
- 18832954
- 00211575
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
-
- Abstract License Flag
- Disallowed