CFRP/Al接着接合継手のモードII疲労き裂進展特性に及ぼす接着剤物性の影響

DOI Web Site

書誌事項

タイトル別名
  • Effect of Mechanical Properties of Adhesive on Mode II Fatigue Crack Growth Behavior in Adhesively Bonded CFRP/Al Joints

抄録

<p>Evaluation error of energy release rate that caused by deformation by shearing force in ENF tests was minimized by proposed method. The exponent of mode II fatigue crack growth curve in adhesively bonded joints that used brittle adhesives is smaller than used ductile adhesives. Microscopic fracture morphology of brittle adhesive was not depend on crack growth rate, however, ductile adhesive depend on that.</p>