Effect of Solid Oxygen Source Species on the Al-Oxide Precipitation Behavior in Fe-Al Alloys by Powder Metallurgy
-
- SATO Katsuhiro
- Graduate School of Engineering, Tohoku University
-
- SEKIDO Nobuaki
- Graduate School of Engineering, Tohoku University
-
- YOSHIMI Kyosuke
- Graduate School of Engineering, Tohoku University
Bibliographic Information
- Other Title
-
- 粉末冶金法を用いたFe-Al合金におけるAl酸化物析出と固体酸素源種の影響
- フンマツ ヤキンホウ オ モチイタ Fe-Al ゴウキン ニ オケル Al サンカブツ セキシュツ ト コタイ サンソ ゲンシュ ノ エイキョウ
Search this article
Abstract
<p>Fe-Al alloy powder was mixed with Fe2O3, NiO and SiO2 powders, and the mixed powders were cold-pressed and annealed at 800°C. Nano-sized Al-oxides were precipitated within the α-Fe matrix of the Fe-Al alloy powder mixed with Fe2O3 and NiO. On the other hand, oxide precipitation was not confirmed within the α-Fe matrix of the SiO2 doped alloy. This difference is caused by the thermodynamic stability of the oxides, where Fe2O3 and NiO are not in equilibrium with α-Fe so that they are dissolved in the α-Fe matrix to form more stable Al-oxides, while SiO2 is in equilibrium with α-Fe thus the chemical driving force for the Al-oxide precipitation was small.</p>
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 66 (10), 478-484, 2019-10-15
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390845702298758656
-
- NII Article ID
- 130007728612
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 030044311
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed