Anodic Characterization of Nickel-Nickel Oxide Composite Materials Prepared by Sintering and Dispersion Coating Method
-
- TASAKA Akimasa
- Doshisha University, Faculty of Engineering, Department of Molecular Science and Technology
-
- TAKEBAYASHI Hitoshi
- Doshisha University, Faculty of Engineering, Department of Molecular Science and Technology
-
- KONDO Satoko
- Doshisha University, Faculty of Engineering, Department of Molecular Science and Technology
-
- TAKEMURA Hideaki
- Doshisha University, Faculty of Engineering, Department of Molecular Science and Technology
-
- YAMAGUCHI Osamu
- Doshisha University, Faculty of Engineering, Department of Molecular Science and Technology
この論文をさがす
説明
<p>The effect of nickel oxide such as NiO1+x and LiNiO2 in the Ni based composite anode on the physico-chemical properties of oxidized layer formed on the composite anode prepared by sintering or dispersion coating method was studied. The galvanostatic and potentiostatic polarization behaviors of the Ni, the Ni-NiO, and the Ni-LiNiO2 composite anodes were investigated to elucidate the anodic processes. The electrical conductivity of the oxidized layer formed on the Ni-NiO and the Ni-LiNiO2 composite anodes was large in a well dehydrated melt of NH4F·2HF and its resistance to corrosion during polarization at potentials higher than 4.6 V vs. H2 was high compared with those on the Ni anode, because of the higher content of nickel oxide in the oxidized layer on the anode.</p>
収録刊行物
-
- Electrochemistry
-
Electrochemistry 67 (6), 628-634, 1999-06-05
公益社団法人 電気化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390845702322842240
-
- NII論文ID
- 10002567610
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 4743812
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可