鍛造Ni基超合金 Udimet 720Liにおける析出相形態の定量的評価

DOI Web Site Web Site 被引用文献2件 参考文献23件

書誌事項

タイトル別名
  • Microstructure Quantification in Wrought Ni-Based Superalloy Udimet 720Li
  • タンゾウ Niキ チョウゴウキン Udimet 720Li ニ オケル セキシュツ ソウギョウタイ ノ テイリョウテキ ヒョウカ

この論文をさがす

抄録

<p>The morphology of γ′ precipitates was quantitatively evaluated for wrought Ni-based superalloy Udimet 720Li by using the absolute moment invariant technique. The diameter of secondary γ′ precipitates, d, increases continuously with the decrease of cooling rate, v, after the solution treatment at 1473 K/1 h along the following equation; d ∝ v-0.4. It is found that the secondary γ′ precipitates changes from spherical to octo-dendrite in shape with the decrease of cooling rate. In the case of oil-quenched alloy after the solution treatment, the value of d continuously increases with aging time at 1173 K, while the spherical shape remains unchanged during aging. On the contrary, for the furnace-cooled alloy, the shape of secondary γ′ precipitates evolves from octo-dendrite to spherical in shape with aging time under the almost constant value of d.</p>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 82 (10), 375-383, 2018-10-01

    公益社団法人 日本金属学会

被引用文献 (2)*注記

もっと見る

参考文献 (23)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ