相状態-粘度測定装置の開発と有機修飾シリカ-ポリスチレン系の粘度測定

DOI
  • 本間 哲雄
    八戸工業高等専門学校
  • 今 千尋
    八戸工業高等専門学校 マテリアル・バイオ工学コース 学生
  • 相野 幸輝
    八戸工業高等専門学校 マテリアル・バイオ工学コース 学生

書誌事項

タイトル別名
  • Viscosities and phase behavior of polystyrene – organic hybridized silica nanoparticle system via rotational viscometer.

抄録

Viscosities and phase behavior of polystyrene – organic hybridized silica nanoparticle at 270 °C were measured with a newly developed visible windows equipped rotational viscometer. The improvement of selection and mounting for the rotary shaft coupling decreased the fluctuation of viscosity measurements. Organic hybridized silica nanoparticles were obtained by treating phenyltrimethoxysilane and silica nanoparticle. The formation of organic hybridized silica nanoparticles were confirmed by using TG-DTA and FT-IR. The viscosities of polystyrene – organic hybridized silica nanoparticles were increased with the mass fraction of the organic hybridized nanoparticles, because the melting point of the blend polymer was increased with the mass fraction of the organic hybridized nanoparticles. The phase behavior of the polystyrene – organic hybridized silica nanoparticle were carried out by the view window, however, no homogeneous states of the blend polymer were found due to the increase of the melting point and the lack of heating temperature. In the future work, we have to optimize the melting temperature and equilibration time for the polystyrene – organic hybridized silica nanoparticle system.

収録刊行物

詳細情報 詳細情報について

  • CRID
    1390845713012772480
  • NII論文ID
    130007500188
  • DOI
    10.24704/hnctech.52.0_85
  • ISSN
    24332003
    03854124
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ