アルミニウム合金ダイカスト表面のX線残留応力測定値の熱処理による変化

DOI Web Site

書誌事項

タイトル別名
  • Residual Stress Measurement on Surfaces of Aluminum Alloy Die Castings with X-ray and its Changes by Heat Treatment
  • アルミニウム ゴウキン ダイカスト ヒョウメン ノ Xセン ザンリュウ オウリョク ソクテイチ ノ ネツ ショリ ニ ヨル ヘンカ

この論文をさがす

抄録

<p>  The measurement of the residual stress in aluminum alloy die castings by x-ray method was investigated in order to apply this method for improving the analysis accuracy of the deformation of aluminum alloy die castings. The residual stress of one flat type experimental die castings and six kinds of practical die cast products were assessed by the x-ray method. As a result, the stress occurring in a deformed die castings was found to be measurable by the x-ray method. However, the residual stress in the as-cast die castings measured by the x-ray method showed a lower compressive value than that measured by the stress relaxation method in which the die castings was cut off and the residual stress was measured by strain gauges. The cause of the inconsistency between the x-ray method and stress relaxation method was estimated as the decrease in the lattice constants of aluminum measured by x-ray due to the solid solution of silicon and copper in aluminum. Therefore, the x-ray method can be used to measure the residual stress in die castings after being calibrated by the stress relaxation method. The residual stress on the surface of the die castings was found to become tensile stresses after heat treatment at 200℃ or 250℃.</p>

収録刊行物

  • 鋳造工学

    鋳造工学 90 (12), 730-736, 2018-12-25

    公益社団法人 日本鋳造工学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ