書誌事項
- タイトル別名
-
- Time-resolved and <i>In-situ</i> Observation of δ-γ Transformation during Unidirectional Solidification in Fe-C Alloys
- Fe-Cコウ ノ イチホウコウ ギョウコ カテイ ニ オケル d-gヘンタイ ノ ジカン ブンカイ ・ ソノ バ カンサツ
この論文をさがす
説明
<p>Time-resolved and in-situ observations using synchrotron radiation X-rays successfully proved that the massive-like transformation, in which the γ phase was produced through the solid – solid transformation and the partition of substitute elements such as Mn and Si at the δ/γ interface could be negligibly small, was selected in the unidirectional solidification of 0.3 mass%C steel at a pulling rate of 50 μm/s. The massive-like transformation produced fine γ grains in the vicinity of the front of δ/γ interface. The coarse γ grains also grew behind the fine γ grains along the temperature gradient. Distance between the δ/γ front and the advancing front of coarse γ grains was as short as 200 μm. Namely, the fine γ grains disappeared within 10 s by the growth of coarsen γ grains along the temperature gradient. In addition, the observation of the δ/γ interface confirmed that a transition from the diffusion-controlled γ growth to the massive-like growth of γ phase occurred at a growth rate of 5 μm/s. Thus, the massive-like transformation is dominantly selected in the carbon steel during conventional solidification processes.</p>
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 105 (2), 290-298, 2019
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390845713048934144
-
- NII論文ID
- 130007585393
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 029495510
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可