Curling of Sheet in Asymmetric Rolling Investigated by Profile Measurement of Partly Rolled Sheet
-
- Li Ling
- Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
-
- Matsumoto Ryo
- Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
-
- Utsunomiya Hiroshi
- Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
抄録
<p>The curling of a sheet in cold asymmetric rolling was investigated experimentally by interrupted rolling. Influences of speed difference as well as entry table height were studied. The upper and lower profiles of the aluminum sheet obtained by interrupted rolling were measured by a laser profilometer. The contact lengths on both upper and lower surfaces LU and LL were detected from the profiles. The curvature radius of sheet was calculated from the curling profiles. Under differential-speed rolling, the sheet curled to the slower roll side at low reduction in thickness, while it curled to the faster roll side at higher reduction. Meanwhile, LU on the faster (upper) roll surface was longer than LL on the slower (lower) roll surface at low reduction. On the other hand, LU was shorter than LL at higher reduction in thickness. It is found that the ratio of contact length LL/LU is correlated with the curling direction in the differential-speed rolling. If LL/LU < 1, the sheet curls towards the slower roll side, while the sheet curls towards the faster roll side in case of LL/LU > 1.</p>
収録刊行物
-
- ISIJ International
-
ISIJ International 59 (3), 489-495, 2019-03-15
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390845713057979392
-
- NII論文ID
- 130007615598
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可