- Influence of hydrogen on stress corrosion cracking behavior in Al–10Mg alloy
- Al-10Mg ゴウキン ニ オケル オウリョク フショク ワレ キョドウ ニ オヨボス スイソ ノ エイキョウ
この論文をさがす
抄録
<p>It is known that the susceptibility to stress corrosion cracking of Al–Mg alloy increase with increasing Mg content, whereas the strength of Al–10Mg alloy reach to that of 2000 and 7000 series Al alloys. In-situ observation of the stress corrosion cracking of a hydrogen charged Al–10Mg alloy was conducted by using synchrotron X-ray microtomography in SPring-8. The corrosion area and crack were observed in hydrogen charged material with water atmosphere. The corrosion and crack grow up with increasing applied strain. In addition, deformation localization and high hydrostatic strain that was caused by nucleation of nanovoids during deformation was also observed in crack tip. These observations indicated that the stress corrosion cracking of an Al–10Mg alloy occurs due to the influence of hydrogen.</p>
収録刊行物
-
- 軽金属
-
軽金属 69 (4), 223-227, 2019-04-30
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390845713073813376
-
- NII論文ID
- 130007655571
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 029658495
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可