- Continuous Fiber Reinforced Thermoplastics Molding by Melted Thermoplastic-Resin Transfer Molding Process
- ヨウユウ ネツ カソセイ ジュシ オ モチイタ RTM ニ ヨル レンゾク センイ キョウカ ネツ カソセイ ジュシ フクゴウ ザイリョウ ノ セイケイ
この論文をさがす
説明
<p>The application of Fiber Reinforced Thermoplastics (FRTP), which have the advantage of high specific strength and high specific stiffness, is expected to reduce the weight of automobiles. As thermoplastic resin has difficulty in impregnation into fabrics of continuous fibers due to its high viscosity, FRTP products with complicated shapes are usually manufactured by secondary processing of FRTP laminates. As this method uses high-cost FRTP laminates, in which thermoplastic resin is pre-impregnated into fabrics of reinforcing fibers, it is necessary to develop a low-cost FRTP manufacturing process. In previous study, the molding method, by which FRTP can be molded by compression after injection of melted thermoplastic resin into fabrics, was developed. However, due to the high viscosity of thermoplastic resin, this method is limited to fabrics of discontinuous fibers. As the mechanical properties of FRTP depend on the length of the reinforcing fiber, it is necessary to use continuous fiber for superior materials. In this study, Melted Thermoplastic-Resin Transfer Molding (MT-RTM) process, by which FRTP using continuous fiber can be molded at affordable cost, was developed. The effects of molding condition in MT-RTM on the impregnation properties of injected thermoplastic resin into fabrics of continuous fibers were clarified and tensile tests of MT-RTM products were conducted. In MT-RTM, FRTP of complicated shapes with ribs and bosses can be molded integrally by press while keeping the low viscosity of injected resin at mold temperature near the melting point. GFRTP molded by MT-RTM showed good impregnation property and tensile strength equal to that of GF/PA6 laminates molded by press molding.</p>
収録刊行物
-
- 材料
-
材料 68 (8), 628-635, 2019-08-15
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390845713087033216
-
- NII論文ID
- 130007691473
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 029942075
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可