Internal Stress of Plate Martensite Depending on Aspect Ratio via fcc-hcp Martensitic Transformation in Metastable Austenitic Stainless Steels
-
- Wada Yuki
- Department of Materials Science and Engineering, Tokyo Institute of Technology
-
- Nakada Nobuo
- Department of Materials Science and Engineering, Tokyo Institute of Technology
-
- Onaka Susumu
- Department of Materials Science and Engineering, Tokyo Institute of Technology
この論文をさがす
抄録
<p>Internal stress generated by athermal martensitic transformation from fcc (face-centered cubic) to hcp (hexagonal close-packed) was investigated in 18Cr–8Ni metastable austenitic stainless steel. Lattice parameter ratio of hcp-martensite, c/a, formed by subzero treatment was evaluated accurately by means of electron back scatter diffraction technique. The evaluation revealed that hcp-martensite surrounded by fcc-austenite matrix has obviously higher c/a compared with the reference value in the case when hcp-martensite exists in a single body, and the c/a is continuously increased with increasing the aspect ratio of the plate-shaped hcp-martensite. However, additional formation of martensite with bcc (body centered cubic) reduced the c/a of hcp-martensite suddenly. From the point of view of micromechanics, it can be concluded that internal stress is dynamically increased by the thickening of plate martensite on fcc-hcp martensitic transformation, and the subsequent hcp-bcc martensitic transformation is stimulated to accommodate the internal stress.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 61 (1), 61-67, 2020-01-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390846609787566208
-
- NII論文ID
- 130007772512
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 030154689
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可