Vapor-Liquid-Solid成長法を用いて作製したSmBa<sub>2</sub>Cu<sub>3</sub>O<i><sub>y</sub></i>線材のAg添加による液相安定化と超伝導特性

書誌事項

タイトル別名
  • Liquid Phase Stabilization and Superconducting Properties by Adding Ag to SmBa<sub>2</sub>Cu<sub>3</sub>O<i><sub>y</sub></i> Coated Conductors Fabricated by Vapor-Liquid-Solid Growth Technique
  • Vapor-Liquid-Solid成長法を用いて作製したSmBa₂Cu₃O[y]線材のAg添加による液相安定化と超伝導特性
  • Vapor-Liquid-Solid セイチョウホウ オ モチイテ サクセイ シタ SmBa ₂ Cu ₃ O[y]センザイ ノ Ag テンカ ニ ヨル エキソウ アンテイカ ト チョウデンドウ トクセイ

この論文をさがす

抄録

<p>It is necessary to increase the deposition rate in order to reduce the production cost of REBCO coated conductors. The Vapor-Liquid-Solid (VLS) growth technique is a method capable of fabricating a thin film with high-deposition rate and good crystalline orientation owing to a crystal growth through a liquid phase. Increase of oxygen partial pressure (PO2) during the deposition is effective on increase of the deposition rate. However, since melting point of the liquid phase becomes higher with increasing PO2, it is difficult to fabricate a film at the high PO2. In this study, we tried to lower melting point of the liquid phase by adding Ag in the VLS growth technique. By adding Ag to the liquid phase, VLS growth mode in a stable liquid phase became possible even in the high PO2. As a result, we achieved fabrication of a film at a high deposition rate of 26.0 nm/sec with good crystalline orientation and the critical current density (Jc) of the film was improved.</p>

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (7)*注記

もっと見る

関連プロジェクト

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ