- Low-Temperature Densification of Titanium Powder by Pulse-Current Sintering under Cyclic Uniaxial Pressure
- シュウキテキ イチジク アツリョク カ デ ノ パルス ツウデン ショウケツホウ ニ ヨル チタン フンマツ ノ テイオン デ ノ コウミツド ショウケツ
この論文をさがす
抄録
<p>Low-temperature densification of titanium powder was attempted via pulse-current sintering under cyclic uniaxial pressure. The sintering was performed under cyclic or constant uniaxial pressure of 100 MPa and 200 MPa at temperatures of 400°C and 500°C. The effect of the cyclic pressure on the densification of the titanium powder was confirmed under all sintering conditions. When the sintering was performed at 400°C under a uniaxial pressure of 100 MPa, the relative density was 92.2% for sintering under cyclic pressure and as low as 77.3% for sintering under constant pressure. The relative density reached 97.7% through sintering at 500°C under a cyclic uniaxial pressure of 200 MPa. Thus, applying the cyclic uniaxial pressure during the pulse-current sintering is effective for preparing dense sintered titanium at lower temperatures.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 67 (10), 525-528, 2020-10-15
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390849376465256576
-
- NII論文ID
- 130007926124
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 030702282
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可