Relation between Intergranular Stress of Austenite and Martensitic Transformation in TRIP Steels Revealed by Neutron Diffraction
-
- Harjo Stefanus
- J-PARC Center, Japan Atomic Energy Agency
-
- Kawasaki Takuro
- J-PARC Center, Japan Atomic Energy Agency
-
- Tsuchida Noriyuki
- Graduate School of Engineering, University of Hyogo
-
- Morooka Satoshi
- J-PARC Center, Japan Atomic Energy Agency Materials Sciences Research Center, Japan Atomic Energy Agency
-
- Gong Wu
- J-PARC Center, Japan Atomic Energy Agency Elements Strategy Initiative for Structural Materials, Kyoto University
抄録
<p>In situ neutron diffraction measurements of two low-alloy steels and a 304-type stainless steel during tensile and creep tests were performed at room temperature. Changes in the diffraction pattern, the integrated peak intensities of austenite (γ), and the peak positions of γ were analyzed and discussed to elucidate the relationship between intergranular stress in γ and the occurrence of martensitic transformation during deformation. Tensile loading experiments revealed that the susceptibility to martensitic transformation depended on the γ-(hkl) grains, where γ-(111) grains underwent martensitic transformation at the latest. The volume fractions of γ were found to decrease under an applied load but to remain almost unchanged under constant load in creep tests, where the lattice strains of γ-(hkl) grains were mostly unchanged. The γ-hkl dependence of the susceptibility to martensitic transformation was found to be controlled by the shear stress levels in γ-(hkl) grains, which were affected by the intergranular stress partitioning during deformation.</p>
収録刊行物
-
- ISIJ International
-
ISIJ International 61 (2), 648-656, 2021-02-15
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390850092191615744
-
- NII論文ID
- 130007987394
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可