書誌事項
- タイトル別名
-
- Improvement of Density and Young’s Modulus of TiB<sub>2</sub> Reinforced Low-alloyed Sintered Steel by Small Amount Addition of Boride Powder
- ホウ化物の少量複合添加によるTiB₂添加低合金焼結鋼の高密度・高ヤング率化
- ホウカブツ ノ ショウリョウ フクゴウ テンカ ニ ヨル TiB ₂ テンカ テイゴウキン ショウケツコウ ノ コウミツド ・ コウヤングリツカ
この論文をさがす
抄録
<p>To obtain a significantly higher Young’s modulus than conventional wrought steels, the improvement of the sintered density was necessary for low-alloyed sintered steels containing 15 vol% or more TiB2. In this study, the effect of boride powders as the small amount additives on the sintered density and the Young’s modulus of TiB2 reinforced low-alloyed sintered steels was investigated.</p><p>A small amount addition of ZrB2 powder was suitable to increase the sintered density of low-alloyed sintered steels containing 15 vol% or more TiB2, because of promoting the infiltration of the liquid phase formed during sintering into the agglomerates of TiB2 particles. As a result, the high sintered density equivalent to 97% of pore free density and the high Young’s modulus of 300 GPa equivalent to 1.5 times that of conventional wrought steels were achieved when the content of TiB2 was 40 vol%.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 68 (2), 60-66, 2021-02-15
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390850092195887872
-
- NII論文ID
- 130007986291
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 031305056
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可